Table 8: Average maximum strength, strain, strength enhancement, energy absorption, and ductility Factor.
Label |
fco |
fcc |
εco |
εcc |
ε1 |
εcr |
fcc/fco |
εcc/εco |
μcr |
E |
C3 |
16.89 |
|
0.0029 |
|
0.0017 |
0.0033 |
|
|
1.89 |
0.038 |
C3P3H1 |
|
26.99 |
|
0.0098 |
0.0033 |
0.0515 |
1.60 |
3.43 |
15.85 |
1.14 |
C3P4H1 |
|
24.57 |
|
0.0094 |
0.0050 |
0.0650 |
1.45 |
3.32 |
13.00 |
1.11 |
C3P3H2 |
|
24.59 |
|
0.0331 |
0.0060 |
0.10000 |
1.02 |
10.18 |
16.67 |
1.99 |
C3P3H3 |
|
23.15 |
|
0.0175 |
0.0060 |
0.06580 |
0.96 |
5.40 |
30.54 |
1.18 |
C3P3H4 |
|
20.98 |
|
0.0187 |
0.0055 |
0.08600 |
0.87 |
5.76 |
16.23 |
1.29 |
C3D1H1 |
|
22.27 |
|
0.0130 |
0.0065 |
0.0458 |
1.32 |
4.56 |
7.05 |
0.79 |
C3D2H1 |
|
22.29 |
|
0.0090 |
0.0020 |
0.0314 |
1.32 |
3.16 |
15.69 |
0.59 |
C3D3H1 |
|
23.49 |
|
0.0130 |
0.0020 |
0.0891 |
1.39 |
4.56 |
44.56 |
1.73 |
C3D1H2 |
|
20.14 |
|
0.0045 |
0.0015 |
0.0234 |
1.19 |
1.56 |
15.61 |
0.29 |
C3D1H3 |
|
18.37 |
|
0.0124 |
0.0044 |
0.0151 |
1.09 |
4.35 |
3.43 |
0.21 |
C3D3H2 |
|
20.71 |
|
0.0084 |
0.0040 |
0.0247 |
1.23 |
2.95 |
6.17 |
0.39 |
C3D3H3 |
|
18.43 |
|
0.0255 |
0.0130 |
0.0340 |
1.09 |
8.94 |
2.62 |
0.47 |