Table 1: Influence of curing type on UHPC strength performance.
| Research |
Specimen Type |
Curing Type |
Strength Type |
| Heat / Temperature (oC) |
Steam / Autoclave (MPa/ oC) |
Compressive Strength (MPa) |
Flexural Strength (MPa) |
| Heat |
Steam / Autoclave |
Heat |
Steam / Autoclave |
| Chen et al. (2018) |
Beam/ Prism |
20 (room) |
- / 0.5-1.5MPa (156-203 oC) |
114-126 |
- / 110-168 |
16-20 |
- / 16.5-22.5 |
| Alsalman et al. (2017) |
Cube/ Cylinder |
21 (room); 60-90 |
- |
106-115 (150-180); 105-120 (125-150) |
- |
- |
- |
| Wu et al. (2017) |
Beam/ Prism |
20 (room); 90 |
90 / - |
138-150 |
191-201 / - |
27-38 |
30-40 / - |
| Van et al. (2014) |
Beam |
20 (room); 65; 90 |
- |
170-185; 170-185; 170-190 |
- |
- |
- |
| Yang et al. (2009) |
Prism/ Cube |
20 (room); 90 |
- |
100-130; 150-180 |
- |
16-22 / 21-25 |
- |
| Chi and Hu (2003) |
Cylinder |
- |
- / (150-200 oC) |
- |
- / 34-64 |
- |
- |
| Aldea et al. (2000) |
Cylinder |
20 (room) |
80 / 0.5MPa (175 oC) |
26-60 |
24-48 / 38-46 |
- |
- |
Note: strength at 28 days.