Table 1: Experimental Conditions, Crystallite Size, Cell Parameter a and c of TiO2. Surface Areas and Porosity
Sample |
ZrOSO4
[g] |
EDX of Zr
[wt .%] |
Anatase
Crystallite Size
[nm] |
Cell
Par.
a
|
Cell
Par.
c
|
BET
[m2g-1] |
Pore
Radius
[Å] |
Pore
Volume
[ccg-1] |
K at
254 nm
[min-1] |
K at
368 nm
[min-1] |
TiZr_0 |
0 |
- |
4.2 |
3.7860 |
9.5148 |
200.4 |
17.344 |
0.190 |
0.1737 |
0.0434 |
TiZr_1 |
1 |
1.48 |
5.2 |
3.7987 |
9.5306 |
163.3 |
17.338 |
0.162 |
0.0669 |
0.0231 |
TiZr_2 |
3 |
6.78 |
5.4 |
3.8043 |
9.5597 |
167.2 |
17.292 |
0.169 |
0.0748 |
0.0318 |
TiZr_3 |
5 |
8.80 |
6.3 |
3.8129 |
9.5786 |
209.6 |
17.268 |
0.253 |
0.0693 |
0.0343 |
TiZr_4 |
10 |
13.17 |
7.2 |
3.8146 |
9.5860 |
282.3 |
24.640 |
0.352 |
0.0766 |
0.0400 |
TiZr_5 |
15 |
15.22 |
~ 1 |
- |
- |
26.5 |
17.122 |
0.028 |
0.1679 |
0.9799 |
TiZr_6 |
20 |
18.93 |
~ 1 |
- |
- |
211.6 |
16.349 |
0.201 |
0.1158 |
0.0195 |
P25 |
- |
- |
- |
- |
- |
- |
- |
- |
0.0539 |
0.0225 |